| Specificaties Latex
en Nitrile Onderzoekshandschoenen |
| Materiaal |
Rubber Latex |
Rubber Latex |
Rubber Latex |
Rubber Latex |
Acrylonitrile Butadine |
Acrylonitrile Butadine |
| Kleur |
Creamy White |
Natural White |
Creamy White |
Natural White |
Light Blue |
Creamy White |
| Oppervlak afwerking
|
Textured |
Textured |
Smooth |
Smooth |
Textured |
Finger Textured |
| Size |
| X-Small |
X |
X |
X |
X |
X |
X |
| Small |
X |
X |
X |
X |
X |
X |
| Medium |
X |
X |
X |
X |
X |
X |
| Large |
X |
X |
X |
X |
X |
X |
| X-Large |
X |
X |
X |
X |
X |
X |
| Dimensions |
| Length (min) |
240 mm |
240 mm |
240 mm |
240 mm |
240 mm |
240 mm |
| Thickness |
|
|
|
|
|
|
| Fingers |
0.19 mm |
0.19mm |
0.19 mm |
0.18 mm |
0.15 mm |
0.15 mm |
| Palm |
0.17 mm |
0.17 mm |
0.17 mm |
0.15 mm |
0.13 mm |
0.13 mm |
| Physical properties |
| Tensile strength |
| Before Aging |
21 mpa |
21 mpa |
21 mpa |
21 mpa |
14 mpa |
14 mpa |
| After Aging |
18 mpa |
18 mpa |
18 mpa |
18 mpa |
14 mpa |
14 mpa |
| ASTM |
14 mpa |
14 mpa |
14 mpa |
14 mpa |
12,5 mpa |
12,5 mpa |
| Ultimate Elongation |
| Before Aging |
750% |
750% |
750% |
750% |
500% |
500% |
| After Aging |
700% |
720% |
700% |
720% |
400% |
400% |
| Protein Content |
| Latex protein
|
< 50 ug |
< 75 ug |
< 50 ug |
< 200 ug |
- |
- |
| Residual Powder content |
| ASTM |
< 2 mg |
< 2 mg |
< 2 mg |
|
< 2 mg |
< 2 mg |
| AQL |
1,5 |
1,5 |
1,5 |
1,5 |
1,5 |
1,5 |